EPA & CARB Compliant Electronic Fuel Injection (EFI) Hose Rubber Fuel Line

Product:

EPA & Carb Compliant Electronic Fuel Injection (EFI)  Hose Rubber Fuel Line

Item No.:

FST-0001

Size & Shape:

ID≥Φ2.5 mm;
Customized as Required.

Material:

FKM/ECO/AR/ECO

Structure:

Four layers

Color:

Black

Application

Use for Electronic Fuel Injection(EFI) in Engines in Automobiles,Motorcycles,ATV,UTV,Garden Machinery,Outdoor Power Equipments,and so on.

EPA & CARB CERTIFICATE

YES.

Standard

SAE, YDK,HES, EX-S,ASTM and so on

Shipping Port

Xiamen

OEM/ODM

Accepted

Package

PE bag+Carton+Pallet

Payment Terms

T/T, L/C,Western Union

Factory

ISO/IATF16949 registered

Technical Teams

20+ Years experience

Sample Leadtime

7-15 days

Production Leadtime

20-30 days

RUBBER TEST METHODS & SPECIFICATIONS

Unit

Value

EXTRACTABLES

ASTM FULE C,300MM LONG SPECIMENS
METHODS
CONFORM TO 6.5.8

g/m2

2.50 MAX

PERMEATION

ASTM FULE C,
METHODS
CONFORM TO 9.1~9.2

g/m2/24H

15 MAX

BURST

HOSE ID < 9.53mm

MPA

6.2 MIN

HOSE ID  > 9.53mm

MPA

3.4 MIN

VACUUM COLLAPSE

DURING APPLICATION OF VACUUM FOR A MINIMUM OF 15S AND NOT MORE THAN 60S

%

20 MAX

COLD FLEXIBILITY

TO BE DRY HEAT AGED FOR 135℃×70H,AFTER AGING,TO BE CONDITIONED AT -34℃×5H,THEN FLEXED IN THE COLD CHAMBER THROUGH 180 DEGREES FROM THE CNETERLINE TO A DIAMETER OF 10 TIMES THE MAXIMUM OD OF THE HOSE

NOT FRACTURE,
NO CRACKS,
NOCHEKS,
NO BREAKS

OZONE RESISTANCE

SHALL BE ACCORDANCE WITH ASTM D 1149, THE SPECIMEN SHALL BE ALLOWED TO REST IN AN OZONE-FREE FOR 23℃×24H ,AND THE MOUNTED SPECIMEN SHALL BE PLACED IN A TEST CHAMBER CONTAINING OZONE AT 100MPA×40℃,AFTER 70H OF EXPOSURE

NO CRACKS
(BE VISUALLY INSPECTED UNDER 7X MAGNIFICATION)

ADHESION

SEPARATE A 25.4MM WIDTH

N

35.6 MIN

KINK RESISTANCE

300MM LONG SPECIMEN,23℃×2H,BEND HOSE ALONG ITS NATURAL CURVATURE AND INSERT THE OTHER END CAREFULLY INTO THE SECOND HOLE UNTIL IT PROJECTS 63 MM OUT THE OTHER SIDE

PASS

DRY HEAT RESISTANCE

THE HOSE TO SLOWLY STRAIGHTENED(TAKING 7 TO 8S)AFTER BEING EXPOSED AS SHOWN IN FIGURE FOR A PERIOD OF 7 DAYS FOR 150 ℃

NO CRACKS,
NO CHARRING,
NO DISINTEGRATION