Z408 Pure Nickel Cast Iron Electrode AWS ENiFe-CI

Z408 is the cast iron electrode with nickel iron alloy core and strong reduction of graphite coating . It can be used in AC and DC dual purpose, has stable arc,and is easy to operate. The electrode has the characteristics of high strength, good plasticity, low linear expansion coefficient and so on. The crack resistance for grey cast iron is as much as that for Z308, while the crack resistance for nodular cast iron is more than Z308. For cast iron with higher phosphorus (0.2%P), it also has a good results and its tocutting performance is lower than Z308 andZ508 slightly. Z408 is used in the welding of gray iron and nodular cast iron for room

ATTENTION:

Before welding, the electrodes need to be baked for 1 hour with the temperature of 150±10℃ before using.

When welding ,it is appropriate to take narrow weld and each weld length should not exceed 50mm. Hammer the welding area lightly with a hammer immediately after welding in order to eliminate stress and prevent cracks.

Lower heat input is recommend.

Applicable process of cast iron welding rod

1. Proper surface cleaning must be done before welding, and the welded joint should be obliquely cut into a U-shaped groove.
2. Stop crack holes at both ends of the crack to prevent crack expansion during welding.
3. When the angle of repair is not good, you can use WE100 welding rod to cold groove to form an effective U-shaped or V-shaped groove.
4. Weld with as little current as possible, medium arc length, and slightly inclined to the welding direction.
5. It is recommended to use short and thin welding beads and a narrow lateral swing welding torch to fill the weld joint before stopping arc welding. Usually no heat treatment is required and the parts are allowed to cool slowly.

Need a quick quotation for Z408? Chat with us on WhatsApp or email info@steeltoolschina.com.